Polyethylene terephthalate

Source: Wikipedia, the free encyclopedia.
(Redirected from
Dacron
)

Polyethylene terephthalate
Strukturformel von Polyethylenterephthalat (PET)
PET polymer chain
A short section of a PET polymer chain
Names
IUPAC name
poly(ethylene terephthalate)
Systematic IUPAC name
poly(oxyethyleneoxyterephthaloyl)
Other names
Terylene (trademark); Dacron (trademark).
Identifiers
Abbreviations PET, PETE
ChEBI
ChemSpider
  • None
ECHA InfoCard
100.121.858 Edit this at Wikidata
UNII
Properties
(C10H8O4)n[1]
Molar mass 10–50 kg/mol, varies
Density
Melting point > 250 °C (482 °F; 523 K)[2] 260 °C[1]
Boiling point > 350 °C (662 °F; 623 K) (decomposes)
Practically insoluble[2]
log P 0.94540[3]
Thermal conductivity
0.15[4] to 0.24 W/(m·K)[1]
1.57–1.58,[4] 1.5750[1]
Thermochemistry
1.0 kJ/(kg·K)[1]
Related compounds
Related Monomers
Terephthalic acid
Ethylene glycol
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
checkY verify (what is checkY☒N ?)

Polyethylene terephthalate (or poly(ethylene terephthalate), PET, PETE, or the obsolete PETP or PET-P), is the most common

resins.[5]

In 2016, annual production of PET was 56 million tons.[6] The biggest application is in fibres (in excess of 60%), with bottle production accounting for about 30% of global demand.[7] In the context of textile applications, PET is referred to by its common name, polyester, whereas the acronym PET is generally used in relation to packaging.[citation needed] Polyester makes up about 18% of world polymer production and is the fourth-most-produced polymer after polyethylene (PE), polypropylene (PP) and polyvinyl chloride (PVC).[citation needed]

PET consists of repeating (C10H8O4) units. PET is commonly recycled, and has the digit 1 (♳) as its resin identification code (RIC). The National Association for PET Container Resources (NAPCOR) defines PET as: "Polyethylene terephthalate items referenced are derived from terephthalic acid (or dimethyl terephthalate) and mono ethylene glycol, wherein the sum of terephthalic acid (or dimethyl terephthalate) and mono ethylene glycol reacted constitutes at least 90 percent of the mass of monomer reacted to form the polymer, and must exhibit a melting peak temperature between 225 °C and 255 °C, as identified during the second thermal scan in procedure 10.1 in ASTM D3418, when heating the sample at a rate of 10 °C/minute."[8]

Depending on its processing and thermal history, polyethylene terephthalate may exist both as an amorphous (transparent) and as a

semi-crystalline polymer. The semicrystalline material might appear transparent (particle size less than 500 nm) or opaque and white (particle size up to a few micrometers
) depending on its crystal structure and particle size.

One process for making PET uses

polycondensation reaction of the monomers (done immediately after esterification/transesterification) with water as the byproduct.[5]

Young's modulus, E 2800–3100 MPa
Tensile strength
, σt
55–75 MPa
Elastic limit 50–150%
Notch test
3.6
kJ
/m2
Glass transition temperature
, Tg
67–81
°C
Vicat B 82 °C
Linear expansion coefficient
, α
7×10−5 K−1
Water absorption (ASTM) 0.16
Source[1]

Uses

Textiles

Polyester fibres are widely used in the textile industry. The invention of the polyester fibre is attributed to J. R. Whinfield.

E. I. DuPont
launched the brand 'Dacron'. As of 2022, there are many brands around the world, mostly Asian.

Polyester fibres are used in fashion apparel often blended with cotton, as heat insulation layers in thermal wear, sportswear and workwear and automotive upholstery.

Rigid packaging

Plastic bottles made from PET are widely used for soft drinks, both still and sparkling. For beverages that are degraded by oxygen, such as beer, a multilayer structure is used. PET sandwiches an additional polyvinyl alcohol (PVOH) or polyamide (PA) layer to further reduce its oxygen permeability.

Non-oriented PET sheet can be

blister packs.[11] Crystallizable PET withstands freezing and oven baking temperatures.[12]
: 1378  Both amorphous PET and BoPET are transparent to the naked eye. Color-conferring dyes can easily be formulated into PET sheet.

PET is permeable to oxygen and carbon dioxide and this imposes shelf life limitations of contents packaged in PET.[13]: 104 

In the early 2000s, the global PET packaging market grew at a compound annual growth rate of 9% to €17 billion in 2006.[14]

Flexible packaging

packaging and thermal insulation (such as space blankets
).

Photovoltaic modules

BOPET is used in the backsheet of

photovoltaic modules. Most backsheets consist of a layer of BOPET laminated to a fluoropolymer or a layer of UV stabilized BOPET.[15]

PET is also used as a substrate in thin film solar cells.

Thermoplastic resins

PET can be compounded with glass

fibre and crystallization accelerators, to make thermoplastic resins. These can be injection moulded into parts such as housings, covers, electrical appliance components and elements of the ignition system.[16]

Other applications

  • A waterproofing barrier in
    undersea cables
    .
  • As a film base.
  • As a fibre, spliced into bell rope tops to help prevent wear on the ropes as they pass through the ceiling.
  • Since late 2014 as liner material in type IV composite high pressure gas cylinders. PET works as a much better barrier to oxygen than earlier used (LD)PE.[17]
  • As a 3D printing filament, as well as in the 3D printing plastic PETG (polyethylene terephthalate glycol). In 3D printing PETG has become a popular material[18] - used for high-end applications like surgical fracture tables[19] to automotive and aeronautical sectors, among other industrial applications.[20] The surface properties can be modified to make PETG self-cleaning for applications like the fabrication of traffic signs for the manufacture of light-emitting diode LED spotlights.[21]
  • As one of three layers for the creation of glitter; acting as a plastic core coated with aluminum and topped with plastic to create a light reflecting surface,[22] although as of 2021 many glitter manufacturing companies have begun to phase out the use of PET after calls from organizers of festivals to create bio-friendly glitter alternatives.[22][23]
  • Film for tape applications, such as the carrier for magnetic tape or backing for pressure-sensitive adhesive tapes. Digitalization has caused the virtual disappeance of the magnetic audio and videotape application.
  • Water-resistant paper.[24]
  • PET preform for injection stretch blow moulding of a bottle
    PET preform for injection stretch blow moulding of a bottle
  • A finished PET bottle
    A finished PET bottle
  • A PET bottle which has been heated by a candle and has recrystallized, making it opaque.
    A PET bottle which has been heated by a candle and has recrystallized, making it opaque.
  • PET clamshell packaging, used to sell fruit, hardware, etc.
    PET clamshell packaging, used to sell fruit, hardware, etc.
  • Polyester yarn
    Polyester yarn
  • Microfiber towels and cleaning cloths
    Microfiber towels and cleaning cloths
  • Aluminized Mylar balloons filled with helium
    Aluminized Mylar balloons filled with helium

History

PET was patented in 1941 by John Rex Whinfield, James Tennant Dickson and their employer the Calico Printers' Association of Manchester, England. E. I. DuPont de Nemours in Delaware, United States, first used the trademark Mylar in June 1951 and received registration of it in 1952.[25] It is still the best-known name used for polyester film. The current owner of the trademark is DuPont Teijin Films.[26]

In the Soviet Union, PET was first manufactured in the laboratories of the Institute of High-Molecular Compounds of the

USSR Academy of Sciences in 1949, and its name "Lavsan" is an acronym thereof (лаборатории Института высокомолекулярных соединений Академии наук СССР).[27]

The PET bottle was invented in 1973 by Nathaniel Wyeth[28] and patented by DuPont.[29]

Physical properties

Sailcloth is typically made from PET fibers also known as polyester or under the brand name Dacron; colorful lightweight spinnakers are usually made of nylon.

PET in its most stable state is a colorless, semi-crystalline resin. However it is intrinsically slow to crystallize compared to other semicrystalline polymers. Depending on processing conditions it can be formed into either amorphous or crystalline articles. Its amenability to drawing makes PET useful in fibre and film applications. Like most aromatic polymers, it has better barrier properties than aliphatic polymers. It is strong and

hygroscopic.[30]

About 60% crystallization is the upper limit for commercial products, with the exception of polyester fibers. Transparent products can be produced by rapidly cooling molten polymer below Tg

glass transition temperature to form an amorphous solid.[31] Like glass, amorphous PET forms when its molecules are not given enough time to arrange themselves in an orderly, crystalline fashion as the melt is cooled. At room temperature the molecules are frozen in place, but, if enough heat energy is put back into them by heating above Tg, they begin to move again, allowing crystals to nucleate
and grow. This procedure is known as solid-state crystallization.

When allowed to cool slowly, the molten polymer forms a more crystalline material. This material has spherulites containing many small crystallites when crystallized from an amorphous solid, rather than forming one large single crystal. Light tends to scatter as it crosses the boundaries between crystallites and the amorphous regions between them, causing the resulting solid to be translucent.

Orientation also renders polymers more transparent. This is why BOPET film and bottles are both crystalline to a degree and transparent.

Amorphous PET crystallizes and becomes opaque when exposed to solvents such as chloroform or toluene.[32]

PET is stoichiometrically a mixture of carbon and H2O, and therefore has been used in an experiment involving laser-driven shock compression which created nanodiamonds and superionic water. This could be a possible way of producing nanodiamonds commercially.[33][34]

Absorption/scalping

PET has an affinity for hydrophobic flavors, and drinks sometimes need to be formulated with a higher flavor dosage, compared to those going into glass, to offset the flavor taken up by the container.[35]: 115  Heavy gauge PET bottles are sometimes returnable for re-use as is practiced in some EU countries, however the propensity of PET to absorb flavors makes it necessary to conduct a "sniffer" test on returned bottles to avoid cross-contamination of flavors.[35]: 115 

Intrinsic viscosity

Different applications of PET require different degrees of polymerization, which can be obtained by modifying the process conditions. The molecular weight of PET is measured by solution viscosity. The preferred method is intrinsic viscosity (IV).[36]

IV is a dimensionless measurement. It is found by extrapolating the relative viscosity (measured in (dℓ/g)) to zero concentration.

Shown below are the IV ranges for the main applications:[37]

Fibers
  • 0.40–0.70: textile
  • 0.72–0.98: technical eg tire cord
Films
Bottles
  • 0.70–0.78: general purpose bottles
  • 0.78–0.85: bottles for carbonated drinks
Monofilaments, engineering plastics
  • 1.00–2.00

Copolymers

PET is copolymerized with other diols or diacids to optimize the properties for particular applications.

For example,

PETG or PET-G (polyethylene terephthalate glycol-modified). It is a clear amorphous thermoplastic that can be injection-molded, sheet-extruded or extruded as filament for 3D printing
. PETG can be colored during processing.

Replacing terephthalic acid (right) with isophthalic acid (center) creates a kink in the PET chain, interfering with crystallization and lowering the polymer's melting point.

Another common modifier is

meta
-) linkage produces an angle in the chain, which also disturbs crystallinity.

Such copolymers are advantageous for certain molding applications, such as

stretch blow molding
("SBM"), which are both clear and crystalline enough to be an adequate barrier to aromas and even gases, such as carbon dioxide in carbonated beverages.

Production

Polyethylene terephthalate is produced from

crude oil. Typically an antimony or titanium compound is used as a catalyst, a phosphite is added as a stabilizer and a bluing agent such as cobalt salt is added to mask any yellowing.[39]

Dimethyl terephthalate (DMT) process

Polyesterification reaction in the production of PET

In the dimethyl terephthalate (DMT) process, DMT and excess MEG are transesterified in the melt at 150–200 °C with a basic catalyst. Methanol (CH3OH) is removed by distillation to drive the reaction forward. Excess MEG is distilled off at higher temperature with the aid of vacuum. The second transesterification step proceeds at 270–280 °C, with continuous distillation of MEG as well.[38]

The reactions can be summarized as follows:

First step
C6H4(CO2CH3)2 + 2 HOCH2CH2OH → C6H4(CO2CH2CH2OH)2 + 2 CH3OH
Second step
n C6H4(CO2CH2CH2OH)2 → [(CO)C6H4(CO2CH2CH2O)]n + n HOCH2CH2OH

Terephthalic acid (PTA) process

Polycondensation reaction in the production of PET

In the terephthalic acid process, MEG and PTA are esterified directly at moderate pressure (2.7–5.5 bar) and high temperature (220–260 °C). Water is eliminated in the reaction, and it is also continuously removed by distillation:[38]

n C6H4(CO2H)2 + n HOCH2CH2OH → [(CO)C6H4(CO2CH2CH2O)]n + 2n H2O

Bio-PET

Bio-PET is the

bio-based counterpart of PET.[40][41] Essentially in Bio-PET, the MEG is manufactured from ethylene derived from sugar cane ethanol. A better process based on oxidation of ethanol has been proposed,[42] and it is also technically possible to make PTA from readily available biobased furfural.[43]

Degradation

PET is subject to degradation during processing. If the moisture level is too high, hydrolysis will reduce the molecular weight by chain scission, resulting in brittleness.

If the residence time and/or melt temperature are too high, then thermal degradation or thermooxidative degradation will occur resulting in:

Mitigation measures include

Acetaldehyde

Acetaldehyde is a colorless, volatile substance with a fruity smell. Although it forms naturally in some fruit, it can cause an off-taste in bottled water. Acetaldehyde forms by degradation of PET through the mishandling of the material. High temperatures (PET decomposes above 300 °C or 570 °F), high pressures, extruder speeds (excessive shear flow raises temperature), and long barrel residence times all contribute to the production of acetaldehyde. Photo-oxidation can also cause the gradual formation acetaldehyde over the object's lifespan. This proceeds via a Type II Norrish reaction.[45]

When acetaldehyde is produced, some of it remains dissolved in the walls of a container and then diffuses into the product stored inside, altering the taste and aroma. This is not such a problem for non-consumables (such as shampoo), for fruit juices (which already contain acetaldehyde), or for strong-tasting drinks like soft drinks. For bottled water, however, low acetaldehyde content is quite important, because, if nothing masks the aroma, even extremely low concentrations (10–20 parts per billion in the water) of acetaldehyde can produce an off-taste.[46]

Biodegradation

At least one species of bacterium in the genus Nocardia can degrade PET with an esterase enzyme.[47] Esterases are enzymes able to cleave the ester bond.[47] Also, the initial degradation of PET can be esterases expressed by Bacillus and Nocardia.[48]

Japanese scientists have isolated a bacterium Ideonella sakaiensis that possesses two enzymes which can break down the PET into smaller pieces that the bacterium can digest. A colony of I. sakaiensis can disintegrate a plastic film in about six weeks.[49][50]

French researchers report developing an improved PET hydrolase that can depolymerize at least 90 percent of PET in 10 hours, breaking it down into monomers.[51][52][53]

An enzyme based on a natural PET-ase was designed with the help of a machine learning algorithm to be able to tolerate pH and temperature changes by the University of Texas at Austin. The PET-ase was found to able to degrade various products and could break them down as fast as 24 hours.[54][55]

Environmental concerns

Resource depletion

Compared to the use of petroleum as fuel, however, the amount of crude oil processed into PET is very small. The total production capacity of PET is around 30 million tons,[56] compared to 4.2 billion tons of crude oil production,[57] thus around 0.7% of crude oil is processed into PET.

End of life

Recycle

PET bottles lend themselves well to recycling (see below). In many countries PET bottles are recycled to a substantial degree,[58] for example about 75% in Switzerland.[59] The term rPET is commonly used to describe the recycled material, though it is also referred to as R-PET or post-consumer PET (POSTC-PET).[60][61]

Energy recovery

PET is a desirable fuel for waste-to-energy plants, as it has a high calorific value which helps to reduce the use of primary resources for energy generation.[62]

Littering

Nevertheless, littering has become a prominent issue in public opinion, and PET bottles are a visible part of that.

Dumping of apparel

A substantial amount of post consumer waste from the textile industry ends up in landfills in developing countries such as Chile[63] and in countries in West Africa such as Ghana.[64] PET being a substantial component of apparel, this waste in landfills contains much PET.

Microfibres from apparel and microplastics

Clothing sheds microfibres in use, during washing and machine drying. Plastic litter slowly forms small particles. Microplastics which are present on the bottom of the river or seabed can be ingested by small marine life, thus entering the food chain. As PET has a higher density than water, a significant amount of PET microparticles may be precipitated in sewage treatment plants. PET microfibers generated by apparel wear, washing or machine drying can become airborne, and be dispersed into fields, where they are ingested by livestock or plants and end up in the human food supply. SAPEA have declared that such particles 'do not pose a widespread risk'.[65] PET is known to degrade when exposed to sunlight and oxygen.[66] As of 2016, scarce information exists regarding the life-time of the synthetic polymers in the environment.[67]

Safety

Commentary published in Environmental Health Perspectives in April 2010 suggested that PET might yield endocrine disruptors under conditions of common use and recommended research on this topic.[68] Proposed mechanisms include leaching of phthalates as well as leaching of antimony. An article published in

deionized water stored in PET bottles stays within EU's acceptable limit even if stored briefly at temperatures up to 60 °C (140 °F), while bottled contents (water or soft drinks) may occasionally exceed the EU limit after less than a year of storage at room temperature.[69]

Antimony

catalyst in the form of compounds such as antimony trioxide (Sb2O3) or antimony triacetate in the production of PET. After manufacturing, a detectable amount of antimony can be found on the surface of the product. This residue can be removed with washing. Antimony also remains in the material itself and can, thus, migrate out into food and drinks. Exposing PET to boiling or microwaving can increase the levels of antimony significantly, possibly above US EPA maximum contamination levels.[70]
The drinking water limit assessed by WHO is 20 parts per billion (WHO, 2003), and the drinking water limit in the United States is 6 parts per billion.[71] Although antimony trioxide is of low toxicity when taken orally,[72] its presence is still of concern. The Swiss Federal Office of Public Health investigated the amount of antimony migration, comparing waters bottled in PET and glass: The antimony concentrations of the water in PET bottles were higher, but still well below the allowed maximum concentration. The Swiss Federal Office of Public Health concluded that small amounts of antimony migrate from the PET into bottled water, but that the health risk of the resulting low concentrations is negligible (1% of the "tolerable daily intake" determined by the WHO). A later (2006) but more widely publicized study found similar amounts of antimony in water in PET bottles.[73] The WHO has published a risk assessment for antimony in drinking water.[72]

Fruit juice concentrates (for which no guidelines are established), however, that were produced and bottled in PET in the UK were found to contain up to 44.7 μg/L of antimony, well above the EU limits for tap water of 5 μg/L.[74]

Bottle processing equipment

A finished PET drink bottle compared to the preform from which it is made

There are two basic molding methods for PET bottles, one-step and two-step. In two-step molding, two separate machines are used. The first machine injection molds the preform, which resembles a test tube, with the bottle-cap threads already molded into place. The body of the tube is significantly thicker, as it will be inflated into its final shape in the second step using

stretch blow molding
.

In the second step, the preforms are heated rapidly and then inflated against a two-part mold to form them into the final shape of the bottle. Preforms (uninflated bottles) are now also used as robust and unique containers themselves; besides novelty candy, some

Red Cross chapters distribute them as part of the Vial of Life
program to homeowners to store medical history for emergency responders.

In one-step machines, the entire process from raw material to finished container is conducted within one machine, making it especially suitable for molding non-standard shapes (custom molding), including jars, flat oval, flask shapes, etc. Its greatest merit is the reduction in space, product handling and energy, and far higher visual quality than can be achieved by the two-step system.[citation needed]

Polyester recycling

Resin identification code 1
Alternate 1
Alternate 2

Worldwide, 480 billion plastic drinking bottles were made in 2016 (and less than half were recycled).[75]

While most thermoplastics can, in principle, be recycled, PET bottle recycling is more practical than many other plastic applications because of the high value of the resin and the almost exclusive use of PET for widely used water and carbonated soft drink bottling.[58][76] The prime uses for recycled PET are polyester fiber, strapping, and non-food containers.

Because of the recyclability of PET and the relative abundance of post-consumer waste in the form of bottles, PET is rapidly gaining market share as a carpet fiber.[77] Mohawk Industries released everSTRAND in 1999, a 100% post-consumer recycled content PET fiber. Since that time, more than 17 billion bottles have been recycled into carpet fiber.[78] Pharr Yarns, a supplier to numerous carpet manufacturers including Looptex, Dobbs Mills, and Berkshire Flooring,[79] produces a BCF (bulk continuous filament) PET carpet fiber containing a minimum of 25% post-consumer recycled content.

PET, like many plastics, is also an excellent candidate for thermal disposal (incineration), as it is composed of carbon, hydrogen, and oxygen, with only trace amounts of catalyst elements (but no sulfur).

When recycling polyethylene terephthalate or PET or polyester, in general three ways have to be differentiated:

  1. The chemical recycling back to the initial raw materials purified
    bis(2-hydroxyethyl) terephthalate
  2. The mechanical recycling where the original polymer properties are being maintained or reconstituted.
  3. The chemical recycling where transesterification takes place and other glycols/polyols or glycerol are added to make a polyol which may be used in other ways such as polyurethane production or PU foam production[80][81][82][83] In addition, PET can even be recycled chemically into epoxy based products including paints.[84]

Chemical recycling of PET will become cost-efficient only applying high capacity recycling lines of more than 50,000 tons/year. Such lines could only be seen, if at all, within the production sites of very large polyester producers. Several attempts of industrial magnitude to establish such chemical recycling plants have been made in the past but without resounding success. Even the promising chemical recycling in Japan has not become an industrial breakthrough so far. The two reasons for this are: at first, the difficulty of consistent and continuous waste bottles sourcing in such a huge amount at one single site, and, at second, the steadily increased prices and price volatility of collected bottles. The prices of baled bottles increased for instance between the years 2000 and 2008 from about 50 Euro/ton to over 500 Euro/ton in 2008.

Mechanical recycling or direct circulation of PET in the polymeric state is operated in most diverse variants today. These kinds of processes are typical of small and medium-size industry. Cost-efficiency can already be achieved with plant capacities within a range of 5000–20,000 tons/year. In this case, nearly all kinds of recycled-material feedback into the material circulation are possible today. These diverse recycling processes are being discussed hereafter in detail.

Besides chemical contaminants and degradation products generated during first processing and usage, mechanical impurities are representing the main part of quality depreciating impurities in the recycling stream. Recycled materials are increasingly introduced into manufacturing processes, which were originally designed for new materials only. Therefore, efficient sorting, separation and cleaning processes become most important for high quality recycled polyester.

When talking about polyester recycling industry, we are concentrating mainly on recycling of PET bottles, which are meanwhile used for all kinds of liquid packaging like water, carbonated soft drinks, juices, beer, sauces, detergents, household chemicals and so on. Bottles are easy to distinguish because of shape and consistency and separate from waste plastic streams either by automatic or by hand-sorting processes. The established polyester recycling industry consists of three major sections:

  • PET bottle collection and waste separation: waste logistics
  • Production of clean bottle flakes: flake production
  • Conversion of PET flakes to final products: flake processing

Intermediate product from the first section is baled bottle waste with a PET content greater than 90%. Most common trading form is the bale but also bricked or even loose, pre-cut bottles are common in the market. In the second section, the collected bottles are converted to clean PET bottle flakes. This step can be more or less complex and complicated depending on required final flake quality. During the third step, PET bottle flakes are processed to any kind of products like film, bottles, fiber, filament, strapping or intermediates like pellets for further processing and engineering plastics.

Besides this external (post-consumer) polyester bottle recycling, numbers of internal (pre-consumer) recycling processes exist, where the wasted polymer material does not exit the production site to the free market, and instead is reused in the same production circuit. In this way, fiber waste is directly reused to produce fiber, preform waste is directly reused to produce preforms, and film waste is directly reused to produce film.

In 2023 a process was announced for using PET as the basis for

stoichiometrically carbon and H2O, can be turned into a form of carbon containing sheets and nanospheres, with a very high surface area. The process involves holding a mixture of PET, water, nitric acid, and ethanol at a high temperature and pressure for eight hours, followed by centrifugation and drying.[85][86]

PET bottle recycling

The only form of PET that is widely recycled in 2022 is the bottle. These are recycled by 'mechanical recycling' increasingly to bottles but still to other forms such as film or fibre. Other forms of polyester are not (as of 2022) collected in significant quantities.

Significant investments were announced in 2021 and 2022 for chemical recycling of PET by glycolysis, methanolysis,[87][88] and enzymatic recycling[89] to recover monomers. Initially these will also use bottles as feedstock but it is expected that fibres will also be recycled this way in future.[90]

See also

References

  1. ^ .
  2. ^ a b c Record of Polyethylenterephthalat in the GESTIS Substance Database of the Institute for Occupational Safety and Health, accessed on 7 November 2007.
  3. ^ "poly(ethylene terephthalate) macromolecule_msds".
  4. ^ .
  5. ^ .
  6. ^ Saxena, Shalini (19 March 2016). "Newly identified bacteria cleans up common plastic". Ars Technica. Retrieved 21 March 2016.
  7. S2CID 110703061
    .
  8. ^ "What is PET? - NAPCOR". NAPCOR. Retrieved 8 July 2020.
  9. S2CID 137314779
    .
  10. ^ The name Terylene was formed by inversion of (polyeth)ylene ter(ephthalate) and dates to the 1940s. Oxford Dictionary. Terylene was first registered as a UK trademark in April 1946.[citation needed] UK Intellectual Property Office UK00000646992
  11. ^ Pasbrig, Erwin (29 March 2007), Cover film for blister packs, retrieved 20 November 2016
  12. .
  13. .
  14. ^ Patton, Dominique (16 January 2008). "Salzgitter to buy SIG Beverages unit". Beverage Daily. Retrieved 1 November 2023.
  15. ^ "COVEME PHOTOVOLTAIC Backsheets and Frontsheets for PV modules" (PDF). Retrieved 4 March 2022.
  16. ^ "Rynite PET Design Guide" (PDF). DuPont. Retrieved 4 March 2022.
  17. ^ SIPA: Lightweight compressed gas cylinders have plastic liners / PET provides high oxygen barrier https://www.plasteurope.com, 18 November 2014, retrieved 16 May 2017.
  18. ISSN 1517-7076
    .
  19. .
  20. .
  21. .
  22. ^ .
  23. ^ Street, Chloe (6 August 2018). "61 UK festivals are banning glitter - make the switch to eco sparkle". Evening Standard. Retrieved 25 March 2023.
  24. ^ Teijin. "Teijin Develops Eco-friendly Wet-strong Printing Paper Made 100% with Recycled Polyester Derived from Used PET Bottles". Teijin Group. Archived from the original on 25 August 2013. Retrieved 12 March 2013.
  25. ^ Whinfield, John Rex and Dickson, James Tennant (1941) "Improvements Relating to the Manufacture of Highly Polymeric Substances", UK Patent 578,079; "Polymeric Linear Terephthalic Esters", U.S. patent 2,465,319 Publication date: 22 March 1949; Filing date: 24 September 1945; Priority date: 29 July 1941
  26. ^ TEIJIN: Trademarks Archived 2 May 2013 at the Wayback Machine "Mylar and Melinex are the registered trademarks or trademarks of Dupont Teijin Films U.S. Limited Partnership and have been licensed to Teijin DuPont Films Japan Limited"
  27. .
  28. ^ "Nathaniel Wyeth – Got a lot of bottle". www.thechemicalengineer.com. Retrieved 3 March 2022.
  29. ^ Wyeth, N.; Roseveare, R. (15 May 1973). "US patent US3733309 "Biaxially oriented poly(ethylene terephthalate) bottle"".
  30. .
  31. .
  32. .
  33. ^ Leah Crane (10 September 2022). "Blasting plastic with powerful lasers turns it into tiny diamonds". New Scientist.
  34. ^ .
  35. .
  36. ^ .
  37. .
  38. ^ Bio-based drop-in, smart drop-in and dedicated chemicals
  39. ^ Duurzame bioplastics op basis van hernieuwbare grondstoffen
  40. . Retrieved 4 March 2022.
  41. .
  42. .
  43. .
  44. .
  45. ^ .
  46. .
  47. .
  48. ^ "Could a new plastic-eating bacteria help combat this pollution scourge?". The Guardian. 10 March 2016. Retrieved 11 March 2016.
  49. .
  50. .
  51. .
  52. ^ "Scientists Engineer New Plastic-Eating Enzyme | Sci-News.com". Breaking Science News | Sci-News.com. 28 April 2022. Retrieved 2 June 2022.
  53. S2CID 248414531
    .
  54. ^ "PET production capacity worldwide 2024".
  55. ^ "Global oil production in million metric tons 2020".
  56. ^
    S2CID 99732501
    .
  57. ^ "RAPPORT DE GESTION 2019" (PDF) (in French). Swiss PET Recycling Association. p. 5. Retrieved 5 March 2022.
  58. ISSN 0014-3057
    .
  59. ^ "PET and its eco-friendly alternative: rPET". Prevented Ocean Plastic. 8 May 2020. Retrieved 9 October 2022.
  60. PMID 33432280
    .
  61. ^ "Chile's desert dumping ground for fast fashion leftovers". France 24. 8 November 2021. Retrieved 5 March 2022.
  62. ^ "Fast fashion in the U.S. is fueling an environmental disaster in Ghana". CBS News. Retrieved 19 December 2022.
  63. ^ "SAPEA report: Evidence on microplastics does not yet point to widespread risk - ALLEA". Retrieved 5 March 2022.
  64. S2CID 212404939
    .
  65. .
  66. .
  67. .
  68. .
  69. ^ Consumer Factsheet on: Antimony Archived 7 June 2014 at the Wayback Machine, EPA archive 2003-06-23
  70. ^ a b Guidelines for drinking – water quality. who.int
  71. PMID 16470261
    .
  72. .
  73. TheGuardian.com
    , 28 June 2017 (page visited on 20 July 2017).
  74. .
  75. ^ "R-PET: Schweizer Kreislauf – PET-Recycling". www.petrecycling.ch (in French). Retrieved 6 March 2022.
  76. ^ everSTRAND[permanent dead link] Carpet-inspectors-experts.com archive 2008-03-17
  77. ^ Simply Green Carpet – A Berkshire Flooring Brand. simplygreencarpet.com
  78. ^ Makuska, Ricardas (2008). "Glycolysis of industrial poly(ethylene terephthalate) waste directed to bis(hydroxyethylene) terephthalate and aromatic polyester polyols" (PDF). Chemija. 19 (2): 29–34.
  79. ^ "Arropol | Arropol Chemicals". Retrieved 2 January 2019.
  80. S2CID 255634660
    .
  81. .
  82. .
  83. ^ Karmela Padavic-Callaghan (23 August 2023). "Plastic bottles can be recycled into energy-storing supercapacitors". New Scientist.
  84. ^ Wang, Shengnian; et al. (2023). "Upcycling drink bottle waste to ball-sheet Intercalated carbon structures for supercapacitor applications". ACS Fall 2023 - Sessions. American Chemical Society.
  85. ^ Laird, Karen (18 January 2022). "Loop, Suez select site in France for first European Infinite Loop facility". Plastics News. Retrieved 11 March 2022.
  86. ^ Toto, Deanne (1 February 2021). "Eastman invests in methanolysis plant in Kingsport, Tennessee". Recycling Today. Retrieved 11 March 2022.
  87. ^ Page Bailey, mary (24 February 2022). "Carbios and Indorama to build first-of-its-kind enzymatic recycling plant for PET in France". Chemical Engineering. Retrieved 11 March 2022.
  88. S2CID 225374393
    .

External links