Photocatalysis
In
History
Early mentions (1911–1938)
The earliest mention came in 1911, when German chemist Dr. Alexander Eibner integrated the concept in his research of the illumination of zinc oxide (ZnO) on the bleaching of the dark blue pigment, Prussian blue.[2][3] Around this time, Bruner and Kozak published an article discussing the deterioration of oxalic acid in the presence of uranyl salts under illumination,[3][4] while in 1913, Landau published an article explaining the phenomenon of photocatalysis. Their contributions led to the development of actinometric measurements, measurements that provide the basis of determining photon flux in photochemical reactions.[3][5] After a hiatus, in 1921, Baly et al. used ferric hydroxides and colloidal uranium salts as catalysts for the creation of formaldehyde under visible light.[3][6]
In 1938 Doodeve and Kitchener discovered that TiO
2 , a highly-stable and non-toxic oxide, in the presence of oxygen could act as a photosensitizer for bleaching dyes, as
1964–2024
Research in photocatalysis again paused until 1964, when V.N. Filimonov investigated
A breakthrough occurred in 1972, when Akira Fujishima and Kenichi Honda discovered that electrochemical photolysis of water occurred when a TiO
2 electrode irradiated with ultraviolet light was electrically connected to a platinum electrode. As the ultraviolet light was absorbed by the TiO
2 electrode, electrons flowed from the anode to the platinum cathode where hydrogen gas was produced. This was one of the first instances of hydrogen production from a clean and cost-effective source, as the majority of hydrogen production comes from natural gas reforming and gasification.[3][14] Fujishima's and Honda's findings led to other advances. In 1977, Nozik discovered that the incorporation of a noble metal in the electrochemical photolysis process, such as platinum and gold, among others, could increase photoactivity, and that an external potential was not required.[3][15] Wagner and Somorjai (1980) and Sakata and Kawai (1981) delineated hydrogen production on the surface of strontium titanate (SrTiO3) via photogeneration, and the generation of hydrogen and methane from the illumination of TiO
2 and PtO2 in ethanol, respectively.[3][16][17]
For many decades photocatalysis had not been developed for commercial purposes. However, in 2023 multiple patents were granted to a U.S. company, (Pure-Light Technologies, Inc.) that has developed various formulas and processes that allow for widespread commercialization for VOC reduction and germicidal action. [18] Chu et al. (2017) assessed the future of electrochemical photolysis of water, discussing its major challenge of developing a cost-effective, energy-efficient photoelectrochemical (PEC) tandem cell, which would, “mimic natural photosynthesis".[3][19]
Types of photocatalysis
Heterogeneous photocatalysis
In heterogeneous catalysis the
Most heterogeneous photocatalysts are transition metal oxides and semiconductors. Unlike metals, which have a continuum of electronic states, semiconductors possess a void energy region where no energy levels are available to promote recombination of an electron and hole produced by photoactivation in the solid. The difference in energy between the filled valence band and the empty conduction band in the MO diagram of a semiconductor is the band gap.[20] When the semiconductor absorbs a photon with energy equal to or greater than the material's band gap, an electron excites from the valence band to the conduction band, generating a electron hole in the valence band. This electron-hole pair is an exciton.[20] The excited electron and hole can recombine and release the energy gained from the excitation of the electron as heat. Such exciton recombination is undesirable and higher levels cost efficiency.[21] Efforts to develop functional photocatalysts often emphasize extending exciton lifetime, improving electron-hole separation using diverse approaches that may rely on structural features such as phase hetero-junctions (e.g. anatase-rutile interfaces), noble-metal nanoparticles, silicon nanowires and substitutional cation doping.[22] The ultimate goal of photocatalyst design is to facilitate reactions of the excited electrons with oxidants to produce reduced products, and/or reactions of the generated holes with reductants to produce oxidized products. Due to the generation of positive holes (h+) and excited electrons (e-), oxidation-reduction reactions take place at the surface of semiconductors irradiated with light.
In one mechanism of the oxidative reaction, holes react with the moisture present on the surface and produce a hydroxyl radical. The reaction starts by photo-induced exciton generation in the metal oxide (MO) surface by photon (hv) absorption:
- MO + hν → MO (h+ + e−)
Oxidative reactions due to photocatalytic effect:
- h+ + H2O → H+ + •OH
- 2 h+ + 2 H2O → 2 H+ + H2O2
- H2O2→ 2 •OH
Reductive reactions due to photocatalytic effect:
- e− + O2 → •O2−
- •O2− + HO2• + H+ → H2O2 + O2
- H2O2 → 2 •OH
Ultimately, both reactions generate hydroxyl radicals. These radicals are oxidative in nature and nonselective with a redox potential of E0 = +3.06 V.[23] This is significantly greater than many common organic compounds, which typically are not greater than E0 = +2.00 V.[24] This results in the non-selective oxidative behavior of these radicals.
TiO
2, a wide band-gap semiconductor, is a common choice for heterogeneous catalysis. Inertness to chemical environment and long-term photostability has made TiO
2 an important material in many practical applications. Investigation of TiO2 in the rutile (bandgap 3.0 eV) and anatase (bandgap 3.2 eV) phases is common.[21] The absorption of photons with energy equal to or greater than the band gap of the semiconductor initiates photocatalytic reactions. This produces electron-hole (e− /h+) pairs:[21]
Where the electron is in the conduction band and the hole is in the valence band. The irradiated TiO
2 particle can behave as an electron donor or acceptor for molecules in contact with the semiconductor. It can participate in redox reactions with adsorbed species, as the valence band hole is strongly oxidizing while the conduction band electron is strongly reducing.[21]
Homogeneous photocatalysis
In homogeneous photocatalysis, the reactants and the photocatalysts exist in the same phase. The process by which the atmosphere self-cleans and removes large organic compounds is a gas phase homogenous photocatalysis reaction.[25] The ozone process is often referenced when developing many photocatalysts:
Most homogeneous photocatalytic reactions are
Iron complex hydroxy-radical formation using the ozone process is common in the production of hydrogen fuel (similar to Fenton's reagent process done in low pH conditions without photoexcitation):[26]
Complex-based photocatalysts are semiconductors, and operate under the same electronic properties as heterogeneous catalysts.[27]
Plasmonic antenna-reactor photocatalysis
A plasmonic antenna-reactor photocatalyst is a photocatalyst that combines a
A SiO
2 catalyst combined with an Au light absorber accelerated hydrogen sulfide-to-hydrogen reactions. The process is an alternative to the conventional Claus process that operates at 800–1,000 °C (1,470–1,830 °F).[28]
A Fe catalyst combined with a Cu light absorber can produce hydrogen from ammonia (NH
3) at ambient temperature using visible light. Conventional Cu-Ru production operates at 650–1,000 °C (1,202–1,832 °F).[29]
Applications
Photoactive catalysts have been introduced over the last decade, such as TiO
2 and ZnO nano rodes. Most suffer from the fact that they can only perform under UV irradiation due to their band structure. Other photocatalysts, including a graphene-ZnO nanocompound counter this problem.[31]
Paper
Micro-sized ZnO tetrapodal particles added to pilot paper production.[30] The most common are one-dimensional nanostructures, such as nanorods, nanotubes, nanofibers, nanowires, but also nanoplates, nanosheets, nanospheres, tetrapods. ZnO is strongly oxidative, chemically stable, with enhanced photocatalytic activity, and has a large free-exciton binding energy. It is non-toxic, abundant, biocompatible, biodegradable, environmentally friendly, low cost, and compatible with simple chemical synthesis. ZnO faces limits to its widespread use in photocatalysis under solar radiation. Several approaches have been suggested to overcome this limitation, including doping for reducing the band gap and improving charge carrier separation.[32]
Water splitting
Photocatalytic water splitting separates water into hydrogen and oxygen:[33]
- 2 H2O → 2 H2 + O2
The most prevalently investigated material, TiO
2 , is inefficient. Mixtures of TiO
2 and nickel oxide (NiO) are more active. NiO allows a significant explоitation of the visible spectrum.
Self-cleaning glass
2 oxidize organic matter.[37][38] The rough wedge-like TiO
2 surface can be modified with a hydrophobic monolayer of octadecylphosphonic acid (ODP). TiO
2 surfaces that were plasma etched for 10 seconds and subsequent surface modifications with ODP showed a water contact angle greater than 150◦. The surface was converted into a superhydrophilic surface (water contact angle = 0◦) upon UV illumination, due to rapid decomposition of octadecylphosphonic acid coating resulting from TiO
2 photocatalysis. Due to TiO
2 's wide band gap, light absorption by the semiconductor material and resulting superhydrophilic conversion of undoped TiO
2 requires ultraviolet radiation (wavelength <390 nm) and thereby restricts self-cleaning to outdoor applications.[39]
Disinfection and cleaning
- Water disinfection/decontamination,. Adsorbents are placed in packed beds for 18 hours. Spent adsorbents are placed in regeneration fluid, essentially removing organics still attached by passing hot water opposite to the flow of water during adsorption. The regeneration fluid passes through fixed beds of silica gel photocatalysts to remove and decompose remaining organics.
- TiO
2 self-sterilizing coatings (for application to food contact surfaces and in other environments where microbial pathogens spread by indirect contact).[43] - Magnetic TiO
2 nanoparticle oxidation of organiccontaminants agitated using a magnetic field.[44] - Sterilization of surgical instruments and removal of fingerprints from electrical and optical components.[45]
Hydrocarbon production from CO
2
TiO
2 conversion of CO
2 into gaseous hydrocarbons.[46] The proposed reaction mechanisms involve the creation of a highly reactive carbon radical from carbon monoxide and carbon dioxide which then reacts with photogenerated protons to ultimately form methane. Efficiencies of TiO
2 -based photocatalysts are low, although nanostructures such as carbon nanotubes[47] and metallic nanoparticles[48] help.
Paints
ePaint is a less-toxic alternative to conventional antifouling marine paints that generates hydrogen peroxide.
Photocatalysis of organic reactions by polypyridyl complexes,[49] porphyrins,[50] or other dyes[51] can produce materials inaccessible by classical approaches. Most photocatalytic dye degradation studies have employed TiO
2. The anatase form of TiO
2 has higher photon absorption characteristics.[52]
Filtration membranes
Photocatalyst radical generation species allow for the degradation of organic pollutants into non-toxic compounds at a high efficiency. Use of CuO nanosheets to breakdown azo bonds in food dyes is one such example, with 96.99% degradation after only 6 minutes.[53] Degradation of organic matter is a highly applicable property, particularly in waste processing.
The use of photocatalyst TiO2 as a support system for filtration membranes shows promise in improving membrane bioreactors in the treatment of wastewater.[54] Polymer-based membranes have shown reduced fouling and self-cleaning properties in both blended and coated TiO2 membranes. Photocatalyst-coated membranes show the most promise, as the increased surface exposure of the photocatalyst increases its organic degradation activity.[55]
Photocatalysts are also highly effective reducers of toxic
Air Filtration
Light2CAT was a project funded by the European Commission from 2012 to 2015. It aimed to develop a modified TiO
2 that can absorb visible light and include this modified TiO
2 into construction concrete. The TiO
2 degrades harmful pollutants such as NOx into NO3−. The modified TiO2 is in use in Copenhagen and Holbæk, Denmark, and Valencia, Spain. This “self-cleaning” concrete led to a 5-20% reduction in NOx over the course of a year.[57][58]
Quantification
ISO 22197-1:2007 specifies a test method for the measurement of NO
2 removal for materials that contain a photocatalyst or have superficial photocatalytic films.[59]
Specific
Mass spectrometry allows measurement of photocatalytic activity by tracking the decomposition of gaseous pollutants such as nitrogen NOx or CO
2 [61]
See also
- Light harvesting materials
- Photoelectrochemical cell
- Photolysis
- Photocatalytic water splitting
- Photoredox catalysis
- Photoelectrochemical oxidation
- Photosensitizer
References
- .
- ^ Eibner, Alexander (1911). "Action of Light on Pigments I". Chem-ZTG. 35: 753–755.
- ^ ISBN 978-1-4471-5061-9.
- ^ Bruner, L.; Kozak, J. (1911). "Information on the Photocatalysis I The Light Reaction in Uranium Salt Plus Oxalic Acid Mixtures". Elktrochem Agnew P. 17: 354–360.
- ^ Landau, M. (1913). "Le Phénomène de la Photocatalyse". Compt. Rend. 156: 1894–1896.
- .
- .
- ^ Filimonov, V.N. (1964). "Photocatalytic Oxidation of Gaseous Isopropanol on ZnO + TiO
2". Dokl. Akad. Nauk SSSR. 154 (4): 922–925. - .
- .
- .
- ^ Formenti, M.; Julliet F., F.; Teichner SJ, S.J. (1970). "Controlled Photooxidation of Paraffins and Olefins over Anatase at Room Temperature". Comptes Rendus de l'Académie des Sciences, Série C. 270C: 138–141.
- .
- S2CID 4251015.
- doi:10.1063/1.89262.
- .
- .
- ^ R Young. US Patents 11,906,157; 11,680,506;17/393,065
- S2CID 3903962.
- ^ S2CID 53343077.
- ^ ISSN 2073-4344. Text was copied from this source, which is available under a Creative Commons Attribution 3.0 (CC BY 3.0)license.
- .
- .
- ISBN 978-1-118-67075-0, retrieved 2023-04-16
- PMID 33953206.
- ^ ISBN 978-0-12-821192-2, retrieved 2023-04-01
- ISBN 978-0-12-823007-7, retrieved 2023-04-01
- ^ Blain, Loz (2022-11-02). "Light-powered catalyst makes profitable hydrogen from stinky waste gas". New Atlas. Retrieved 2022-11-30.
- ^ Blain, Loz (2022-11-29). "Revolutionary photocatalyst is huge news for green hydrogen and ammonia". New Atlas. Retrieved 2022-11-30.
- ^ ISSN 2213-3437.
- S2CID 216233251.
- ISSN 2073-4344.
- .
- S2CID 225707644.
- ^ "Snapcat Photo Catalytic Oxidation with TIO
2 (2005)". CaluTech UV Air. Retrieved 2006-12-05. - .
- ^ "Photocatalysis Applications of TiO
2". Titanium Information. titaniumart.com. - .
- ISSN 0926-3373.
- S2CID 198742844.
- S2CID 94649652.
- S2CID 118571942.
- .
- PMID 16295874.
- ^ "New visible light photocatalyst kills bacteria, even after light turned off". ScienceDaily.
- .
- PMID 18678032.
- S2CID 53343077.
- ISBN 9783527674145.
- PMID 27005601.
- PMID 29717745.
- ^ Viswanathan, Balasubramanian (December 2017). "Photocatalytic Degradation of Dyes: An Overview". Current Catalysis, 2018, 7, 000-000: 3.
- PMID 33553878.
- ISSN 0376-7388.
- S2CID 225647896.
- PMID 32325680.
- ^ [dead link]Mathiesen, D. (2012). "Final Report Summary - LIGHT2CAT (Visible LIGHT Active PhotoCATalytic Concretes for Air pollution Treatment)". European Commission.
- ^ Light2CAT (2015). "Light2CAT Visible Light Active PhotoCATalytic Concretes for Air Pollution Treatment [YouTube Video]". YouTube. Archived from the original on 2021-12-13.
{{cite web}}
: CS1 maint: numeric names: authors list (link) - ^ "ISO 22197-1:2007". ISO.
- ^ "Unique Gas Analyser Helps to Characterize Photoactive Pigments | CoatingsPro Magazine". www.coatingspromag.com.
- S2CID 10838037.