Indentation plastometry
This article needs additional citations for verification. (October 2022) |
Indentation plastometry is the idea of using an indentation-based procedure to obtain (bulk)
Basic requirements
Capturing of macroscopic (size-independent) properties brings in a requirement[1][2][3][4] to deform a volume of material that is large enough to be representative of the bulk. This depends on the microstructure, but usually means that it must contain “many” grains and is typically of the order of hundreds of microns in linear dimensions. The indentation size effect, in which the measured hardness tends to increase as the deformed volume becomes small, is at least partly due to a failure to interrogate a representative volume. The indenter, which is normally spherical, therefore needs to have a radius in the approximate range of several hundred microns up to a mm or two.
A further requirement concerns the plastic strains generated in the sample. The indentation response must be sensitive to the plasticity characteristics of the material over the strain range of interest, which normally extends up to at least several % and commonly up to several tens of %. The strains created in the sample must therefore also range up to values of this order. This typically requires that the “penetration ratio” (penetration depth over indenter radius) should be at least about 10%. Finally, depending on the hardness of the metal, this in turn requires that the facility should have a relatively high load capability – usually of the order of several kN.
Experimental outcomes
The simplest indentation procedures, which have been in use for many decades, involve the application of a pre-determined load (often from a dead weight), followed by measurement of the lateral size of the residual indent (or possibly its depth). However, many indentation procedures are now based on “instrumented” set-ups, in which the load is progressively ramped up and both load and penetration (displacement) are continuously monitored during indentation. A key experimental outcome is thus the load-displacement curve. Various types of equipment can be used to generate such curves. These include those designed to carry out so-called “nanoindentation” - for which both the load (down to the mN range) and the displacement (commonly sub-micron) are very small. However, as noted above, if the deformed volume is small, then it’s not possible to obtain “bulk” properties. Moreover, even with relatively large loads and displacements, some kind of “compliance correction” may be required, to separate the response of the sample from displacements associated with the loading system.
The other main form of experimental outcome is the shape of the residual indent. As mentioned above, early types of
Solution procedures
Two main approaches have evolved for obtaining stress-strain relationships from experimental indentation outcomes (load-displacement curves or residual indent profiles). The simpler of the two involves direct “conversion” of the load-displacement curve. This is usually done
The other main approach is a more cumbersome one, although with much greater potential for obtaining reliable results. It involves iterative numerical (Finite element method – FEM) modelling of the indentation procedure. This is first done with a trial stress-strain relationship (in the form of an analytical expression – often termed a constitutive equation), followed by convergence on the best fit version (set of parameter values in the equation), giving optimal agreement between experimental and modelled outcomes (load-displacement plots or residual indent profiles). This procedure fully captures the complexity of the evolving stress and strain fields during indentation. While it is based on relatively intensive modelling computations, protocols have been developed in which the convergence is automated and rapid.
Profilometry-based indentation plastometry (PIP)
It has become clear that important advantages are offered by using the residual indent profile as the target outcome, rather than the load-displacement curve. These include easier measurement, greater sensitivity of the experimental outcome to the stress-strain relationship and potential for detection and characterisation of sample anisotropy – see above. The figure gives an indication of the sensitivity of the profile to the stress-strain curve of the material. The term PIP thus encompasses the following features: 1) Obtaining stress-strain curves characteristic of the bulk of a material (by using relatively large spherical indenters and relatively deep penetration), 2) Experimental measurement of the residual indent profile and 3) Iterative FEM simulation of the indentation test, to obtain the stress-strain curve (captured in a constitutive equation) that gives the best fit between modelled and measured profiles.
For tractable and user-friendly application, an integrated facility is needed, in which the procedures of indentation, profilometry and convergence on the optimal stress-strain curve are all under automated control