Chromate conversion coating

Source: Wikipedia, the free encyclopedia.
Not to be confused with Chrome plating or Diffusion hardening.
Zinc chromate conversion coating on small steel parts.

Chromate conversion coating or alodine coating is a type of

electrical conductivity. It also provides some resistance to abrasion and light chemical attack (such as dirty fingers) on soft metals.[2]

Chromate conversion coatings are commonly applied to items such as screws, hardware and tools. They usually impart a distinctively iridescent, greenish-yellow color to otherwise white or gray metals. The coating has a complex composition including chromium salts, and a complex structure.[2]

The process is sometimes called alodine coating, a term used specifically[2] in reference to the trademarked Alodine process of Henkel Surface Technologies.[3]

Process

Chromate conversion coatings are usually applied by immersing the part in a chemical bath until a film of the desired thickness has formed, removing the part, rinsing it and letting it dry. The process is usually carried out at room temperature, with a few minutes of immersion. Alternatively, the solution can be sprayed, or the part can be briefly dipped in the bath, in which case the coating reactions take place while the part is still wet.[2]

The coating is soft and gelatinous when first applied, but hardens and becomes hydrophobic as it dries, typically in 24 hours or less.[2] Curing can be accelerated by heating to 70 °C (158 °F), but higher temperature will gradually damage the coating on steel.

Bath composition

The composition of the bath varies greatly, depending on the material to be coated and the desired effect. Most bath formulae are proprietary.

The formulations typically contain hexavalent chromium compounds, such as chromates and dichromates.[4]

The widely used

mL/L concentrated sulfuric acid.[5]

Chemistry

The chromate coating process starts with a

redox reaction between the hexavalent chromium and the metal.[2]
In the case of aluminum, for example,

Cr6+
 + Al0 → Cr3+
 + Al3+

The resulting trivalent cations react with

hydroxides, or a solid solution
of both hydroxides:

Cr3+
 + 3 OH−
 → Cr(OH)
3
Al3+
 + 3 OH−
 → Al(OH)
3

Under appropriate conditions, these hydroxides condense with elimination of water to form a

chelating agents and counterions.[2]

The gel film contracts as it dries, compressing the skeleton and causing it to stiffen. Eventually shrinkage stops, and further drying leaves the pores open but dry, turning the film into a

nm thick.[2][6][7]

The coating contracts as it dries, which causes it to crack into many microscopic scales, described as "dried mud" pattern. The trapped solution keeps reacting with any metal that gets exposed in the cracks, so that the final coating is continuous and covers the entire surface.[2]

Although the main reactions turn most of the chromium(VI) anions (chromates and dichromates) in the deposited gel into insoluble chromium(III) compounds, a small quantity of them remains un-reacted in the dried-out coating. For example, in the coating formed on aluminum by a commercial bath, about 23% of the chromium atoms were found to be hexavalent Cr6+
, except in a region close to the metal. These chromium(VI) residues can migrate when the coating is wetted, and are believed to play a role in preventing corrosion in the finished part—specifically, by restoring the coating in any new microscopic cracks where corrosion could start.[2][6][7]

Substrates

Zinc

"Zinc yellow" redirects here. For the RAL color, see
RAL 1018 Zinc yellow
.

Chromating is often performed on

white corrosion, thus making the part considerably more durable, depending on the chromate layer's thickness.[8][9][10]

The protective effect of chromate coatings on zinc is indicated by color, progressing from clear/blue to yellow, gold, olive drab and black. Darker coatings generally provide more corrosion resistance.[11] The coating color can also be changed with dyes, so color is not a complete indicator of the process used.

ISO 4520 specifies chromate conversion coatings on electroplated zinc and cadmium coatings. ASTM B633 Type II and III specify zinc plating plus chromate conversion on iron and steel parts. Recent revisions of ASTM B633 defer to ASTM F1941 for zinc plating mechanical fasteners, like bolts, nuts, etc. 2019 is the current revision for ASTM B633 (superseded the revision from 2015), which raised required tensile thresholds when confronting hydrogen embrittlement issues and addressed embrittlement concerns in a new appendix.

Aluminium and its alloys

For aluminum, the chromate conversion bath can be simply a solution of chromic acid. The process is rapid (1–5 min), requires a single ambient temperature process tank and associated rinse, and is relatively trouble free.[2]

As of 1995, Henkel's Alodine 1200s commercial formula for aluminum consisted of 50-60%

chromic anhydride CrO
3, 20-30% potassium tetrafluoroborate KBF
4, 10-15% potassium ferricyanide K
3Fe(CN), 5-10% potassium hexafluorozirconate K
2ZrF
6, and 5-10% sodium fluoride NaF by weight. The formula was meant to be dissolved in water at the concentration of 9.0 g/L, giving a bath with pH = 1.5. It yielded a light gold color after 1 min, and a golden-brown film after 3 min. The average thickness ranged between 200 and 1000 nm.[6]

Iridite 14-2 is a chromate conversion bath for aluminum. Its ingredients include chromium(IV) oxide, barium nitrate, sodium silicofluoride and ferricyanide.[12] In the aluminum industry, the process is also called chemical film[13] or yellow iridite,[13] Commercial trademarked names include Iridite[13] and Bonderite[14] (formerly known as Alodine, or Alocrom in the UK).[15] The main standards for chromate conversion coating of aluminium are MIL-DTL-5541 in the US, and Def Stan 03/18 in the UK.

Magnesium

Alodine may also refer to chromate-coating magnesium alloys.[3]

Steel

Steel and iron cannot be chromated directly. Steel plated with zinc or zinc-aluminum alloy may be chromated.[9][10] Chromating zinc plated steel does not enhance zinc's cathodic protection of the underlying steel from rust.[5]

Phosphate coatings

Chromate conversion coatings can be applied over the phosphate conversion coatings often used on ferrous substrates. The process is used to enhance the phosphate coating.[5]

Safety

Hexavalent chromium compounds have been the topic of intense workplace and public health concern for their carcinogenicity, and have become highly regulated.[16]

In particular, concerns about the exposure of workers to chromates and dichromates while handling the immersion bath and the wet parts, as well as the small residues of those anions that remain trapped in the coating, have motivated the development of alternative commercial bath formulations that do not contain hexavalent chromium;[17] for instance, by replacing the chromates by trivalent chromium salts, which are considerably less toxic. However, these do not seem to provide the long-term corrosion protection of the traditional formula.[7]

In Europe, the

RoHS and REACH
Directives encourage elimination of hexavalent chromium in a broad range of industrial applications and products, including chromate conversion coating processes.

References

  1. ^ K.H. Jürgen, Buschow, Robert W. Cahn, Merton C. Flemings, Bernhard Ilschner, Edward J. Kramer, and Subhash Mahajan (2001): Encyclopedia of Material – Science and Technology, Elsevier, Oxford, UK.
  2. ^
    doi:10.1016/S0300-9440(01)00143-6
  3. ^ a b Henkel Alodine products home page, accessed 2009-03-27
  4. ISBN 9781566773355
  5. ^
    ISBN 0-904477-16-9
    .
  6. ^
    doi:10.1016/0010-938X(94)00101-B
  7. ^
    doi:10.1016/S0257-8972(01)01003-9
  8. doi:10.1016/S0257-8972(96)03013-7
  9. ^
    doi:10.1016/S0257-8972(03)00847-8
  10. ^
    doi:10.1016/S0169-4332(03)00572-5
  11. ISBN 0-471-65653-4
    .
  12. ^ MacDermid MSDS for Iridite 14-2, Product number 178659.
  13. ^ a b c "Iridite Chromate Conversion Coating Finish Mil-C-5541 Specification | Engineers Edge".
  14. ^ "Aircraft Structures – Alodine Coating". Special Airworthiness Information Bulletin (SAIB): HQ-18-09. FAA. February 5, 2018. Archived from the original (pdf) on 2022-08-15. Retrieved 2018-04-03.
  15. ^ New surface treatment for aluminum. Anthony, J. Iron Age (1946), 158(23), 64-7.
  16. ^ Occupational Exposure to Hexavalent Chromium, US Dept. of Labor, OSHA Federal Register # 71:10099-10385, 28 Feb 2006.
  17. ^ "Archived copy" (PDF). Archived from the original (PDF) on 2011-02-05. Retrieved 2010-09-15.{{cite web}}: CS1 maint: archived copy as title (link)

External links