Aluminium oxynitride
 Spinel structure of ALON
| |
| Names | |
|---|---|
| Systematic IUPAC name
Aluminium oxynitride | |
| Identifiers | |
| Abbreviations | ALON |
| Properties | |
| (AlN)x·(Al2O3)1−x, 0.30 ≤ x ≤ 0.37 | |
| Appearance | White or transparent solid |
| Density | 3.691–3.696 cm3[1]
|
| Melting point | ~2150 °C[1] |
| insoluble | |
Refractive index (nD)
|
1.79[2] |
| Structure | |
| cubic spinel | |
a = 794.6 pm[2]
| |
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
| |
Aluminium oxynitride (marketed under the name ALON by
Aluminium oxynitride is the hardest polycrystalline transparent ceramic available commercially.[2] Because of its relatively low weight, distinctive optical and mechanical properties, and resistance to oxidation or radiation, it shows promise for applications such as bulletproof, blast-resistant, and optoelectronic windows.[4] Aluminium oxynitride-based armor has been shown to stop multiple armor-piercing projectiles of up to .50 BMG.[5]
Properties
Aluminium oxynitride is resistant to various acids, bases, and water.[6]
Mechanical
Aluminium oxynitride has the following mechanical properties:[2]
- Compressive strength 2.68 GPa
- Flexural strength 0.38–0.7 GPa
- Fracture toughness 2.0 MPa·m1/2
- Knoop hardness1800 kg/mm2 (0.2 kg load)
- Poisson ratio0.24
- Shear modulus 135 GPa
- Young's modulus 334 GPa
Thermal and optical
Aluminium oxynitride has the following thermal and optical properties:[7]
- Specific heat0.781 J/(g·°C)
- Thermal conductivity12.3 W/(m·°C)
- Thermal expansion coefficient~4.7×10−6/°C
- Transparency range 200–5000 nm
Applications
Aluminium oxynitride is used for infrared-optical windows, with greater than 80% transparency at wavelengths below about 4 micrometers, dropping to near zero at about 6 micrometers.[8] It has also been demonstrated as an interface passivation layer in some semiconductor-related applications.[9]
Aluminium oxynitride has less than half the weight and thickness of glass-based transparent armor.[10] Aluminium oxynitride armor of 1.6-inch (41 mm; 4.1 cm) thickness is capable of stopping .50 BMG armor-piercing rounds, which can penetrate 3.7 inches (94 mm; 9.4 cm) of traditional glass laminate.[8][11]
In 2005, the United States Air Force began testing aluminium oxynitride-based armor.[12]
Manufacture
Aluminium oxynitride can be fabricated as windows, plates, domes, rods, tubes and other forms using conventional ceramic powder processing techniques. Its composition can vary slightly: the aluminium content from about 30% to 36%, which has been reported to affect the bulk and shear moduli by only 1–2%.
Patents
Patents related to aluminium oxynitride include:
- Aluminium oxynitride having improved optical characteristics and method of manufacture TM Hartnett, RL Gentilman U.S. patent 4,481,300, 1984
- Process for producing polycrystalline cubic aluminium oxynitride JW McCauley U.S. patent 4,241,000, 1980
- Transparent aluminium oxynitride and method of manufacture RL Gentilman, EA Maguire U.S. patent 4,520,116, 1985; U.S. patent 4,720,362, 1988
- Transparent aluminium oxynitride-based ceramic article JP Mathers U.S. patent 5,231,062, 1993
See also
References
- ^ a b "ALON Optical Ceramic. Technical data" (PDF). Surmet Corporation. 2003. Archived from the original (PDF) on 2013-06-12. Retrieved 2009-01-09.
- ^ a b c d Mohan Ramisetty et al. Transparent Polycrystalline Spinels Protect and Defend, American Ceramic Society Bulletin, vol.92, 2, 20–24 (2013)
- ^ 4520116, Richard L. Gentilman, Edward A. Maguire, Leonard E. Dolhert, "Transparent aluminum oxynitride and method of manufacture", published May 28, 1985, assigned to Surmet Corp
- ^ "Domes & Infrared Optics". Surmet.
- ^ Ramisetty, Mohan; Sastri, Suri A.; Goldman, Lee (Aug 2013). "Transparent Ceramics Find Wide Use in Optics". Photonics Spectra.
- .
- ^ a b Joseph M. Wahl et al. Recent Advances in ALON Optical Ceramic, Surmet
- ^ S2CID 123044722.
- . Retrieved 2022-02-11.
- ^ Security News (2015-06-03). Optically Clear Aluminium Provides Bulletproof Protection. TSS, 3 June 2015. Retrieved on 2015-07-10 from http://www.tssbulletproof.com/optically-clear-aluminum-provides-bulletproof-protection/ Archived 2018-02-21 at the Wayback Machine.
- ^ "Surmet's ALON Transparent Armor 50 Caliber Test". YouTube. Retrieved 2023-01-09.
- ^ Schogol, Jeff (October 30, 2005). "Air Force testing lighter, transparent ALON armor". Stars and Stripes. Retrieved 2020-06-25.
- .
External links
- Processing of Optically Transparent Aluminum Oxynitride
- "Solubility Limits of La and Y in Aluminum Oxynitride (AlON) at 1870°C". Lior Miller and Wayne D. Kaplan. Department of Materials Engineering, Technion, Haifa, Israel, 2006.
- The Influence of Sintering Additives on the Microstructure and Properties of ALON. Yechezkel Ashuach. Master's Thesis, Technion – Israel Institute of Technology, 2003.