Pentaerythritol tetrakis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)
Names | |
---|---|
Preferred IUPAC name
2,2-Bis({[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoyl]oxy}methyl)propane-1,3-diyl bis[3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoate] | |
Other names
Anox 20, Irganox 1010, Dovernox 10
| |
Identifiers | |
3D model (
JSmol ) |
|
ChEMBL | |
ChemSpider | |
ECHA InfoCard
|
100.027.021 |
EC Number |
|
PubChem CID
|
|
RTECS number
|
|
UNII | |
| |
| |
Properties | |
C73H108O12 | |
Molar mass | 1177.655 g·mol−1 |
Appearance | White solid |
Melting point | 110–125 °C (230–257 °F; 383–398 K) |
<0.1 g/ml | |
Solubility in Acetone | 0.75 g/ml |
Solubility in Toluene | 0.5 g/ml |
Solubility in Methanol | <0.1 g/ml |
Hazards | |
GHS labelling: | |
H413 | |
P273, P501 | |
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
|
Pentaerythritol tetrakis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate) is a chemical compound composed of 4 sterically hindered
stabilizing polymers, particularly polyethylene and polypropylene
.
Synthesis
Base catalysed
2,6-di-tert-butylphenol forms the intermediate butyl-phloretic ester. High temperature transesterification of this with pentaerythritol
gives the final product. Driving this reaction to completion can be difficult and commercial samples often contain low levels of the tri-ester.
Properties
The linking of phenols together with pentaerythritol maintains their activity with greatly reduced volatility. This is important during the processing and molding steps where the plastic is heated to molten, typically several hundred degrees.[1]